1.4104 Stainless Steel X14CrMoS17 Material Properties Equivalent, QT650 vs 6082 Aluminum Alloy 6082-T6 T651 AlMgSi1 (AlSi1MgMn – 3.2315) Properties
Ratings Comparison
Strength
1.4104 Stainless Steel X14CrMoS17 Material Properties Equivalent, QT650
5/10
6082 Aluminum Alloy 6082-T6 T651 AlMgSi1 (AlSi1MgMn – 3.2315) Properties
3/10
Corrosion Resistance
1.4104 Stainless Steel X14CrMoS17 Material Properties Equivalent, QT650
7/10
6082 Aluminum Alloy 6082-T6 T651 AlMgSi1 (AlSi1MgMn – 3.2315) Properties
6/10
Lightweight
1.4104 Stainless Steel X14CrMoS17 Material Properties Equivalent, QT650
5/10
6082 Aluminum Alloy 6082-T6 T651 AlMgSi1 (AlSi1MgMn – 3.2315) Properties
9/10
Machinability
1.4104 Stainless Steel X14CrMoS17 Material Properties Equivalent, QT650
4/10
6082 Aluminum Alloy 6082-T6 T651 AlMgSi1 (AlSi1MgMn – 3.2315) Properties
8/10
Cost Efficiency
1.4104 Stainless Steel X14CrMoS17 Material Properties Equivalent, QT650
6/10
6082 Aluminum Alloy 6082-T6 T651 AlMgSi1 (AlSi1MgMn – 3.2315) Properties
7/10
Temperature Resistance
1.4104 Stainless Steel X14CrMoS17 Material Properties Equivalent, QT650
7/10
6082 Aluminum Alloy 6082-T6 T651 AlMgSi1 (AlSi1MgMn – 3.2315) Properties
4/10
Properties Comparison
| Property | 1.4104 Stainless Steel X14CrMoS17 Material Properties Equivalent, QT650 | 6082 Aluminum Alloy 6082-T6 T651 AlMgSi1 (AlSi1MgMn – 3.2315) Properties |
|---|---|---|
| Metal Base | Stainless Steel | Aluminum |
| Tensile Strength | — | 150.0 MPa |
| Yield Strength | — | 85.0 MPa |
| Elongation | — | 8211.0 % |
| Hardness (Brinell) | — | 40.0 HB |
| Elastic Modulus | — | — |
| Density | — | — |
| Melting Point | — | — |
| Thermal Conductivity | — | — |
| Weldable | — | — |
| Heat Treatable | — | — |
| Magnetic | — | — |