42CrMoS4 +QT (1.7227) Steel 42CrMoS4V Material Properties, Composition, Hardness vs AISI SAE 8620 Steel Properties, Chemical Composition, Equivalent, Heat Treatment
Ratings Comparison
Strength
42CrMoS4 +QT (1.7227) Steel 42CrMoS4V Material Properties, Composition, Hardness
8/10
AISI SAE 8620 Steel Properties, Chemical Composition, Equivalent, Heat Treatment
6/10
Corrosion Resistance
42CrMoS4 +QT (1.7227) Steel 42CrMoS4V Material Properties, Composition, Hardness
3/10
AISI SAE 8620 Steel Properties, Chemical Composition, Equivalent, Heat Treatment
3/10
Lightweight
42CrMoS4 +QT (1.7227) Steel 42CrMoS4V Material Properties, Composition, Hardness
5/10
AISI SAE 8620 Steel Properties, Chemical Composition, Equivalent, Heat Treatment
5/10
Machinability
42CrMoS4 +QT (1.7227) Steel 42CrMoS4V Material Properties, Composition, Hardness
6/10
AISI SAE 8620 Steel Properties, Chemical Composition, Equivalent, Heat Treatment
6/10
Cost Efficiency
42CrMoS4 +QT (1.7227) Steel 42CrMoS4V Material Properties, Composition, Hardness
9/10
AISI SAE 8620 Steel Properties, Chemical Composition, Equivalent, Heat Treatment
9/10
Temperature Resistance
42CrMoS4 +QT (1.7227) Steel 42CrMoS4V Material Properties, Composition, Hardness
7/10
AISI SAE 8620 Steel Properties, Chemical Composition, Equivalent, Heat Treatment
7/10
Properties Comparison
| Property | 42CrMoS4 +QT (1.7227) Steel 42CrMoS4V Material Properties, Composition, Hardness | AISI SAE 8620 Steel Properties, Chemical Composition, Equivalent, Heat Treatment |
|---|---|---|
| Metal Base | Steel | Steel |
| Tensile Strength | 1100.0 MPa | 633.0 MPa |
| Yield Strength | 900.0 MPa | 357.0 MPa |
| Elongation | 10.0 % | 26.3 % |
| Hardness (Brinell) | — | 183.0 HB |
| Elastic Modulus | — | — |
| Density | — | — |
| Melting Point | — | — |
| Thermal Conductivity | — | — |
| Weldable | — | — |
| Heat Treatable | — | — |
| Magnetic | — | — |