42CrMoS4 +QT (1.7227) Steel 42CrMoS4V Material Properties, Composition, Hardness vs Aluminium 6060 T5, T6, T4; Aluminum Alloy 6060 Properties
Ratings Comparison
Strength
42CrMoS4 +QT (1.7227) Steel 42CrMoS4V Material Properties, Composition, Hardness
8/10
Aluminium 6060 T5, T6, T4; Aluminum Alloy 6060 Properties
3/10
Corrosion Resistance
42CrMoS4 +QT (1.7227) Steel 42CrMoS4V Material Properties, Composition, Hardness
3/10
Aluminium 6060 T5, T6, T4; Aluminum Alloy 6060 Properties
6/10
Lightweight
42CrMoS4 +QT (1.7227) Steel 42CrMoS4V Material Properties, Composition, Hardness
5/10
Aluminium 6060 T5, T6, T4; Aluminum Alloy 6060 Properties
9/10
Machinability
42CrMoS4 +QT (1.7227) Steel 42CrMoS4V Material Properties, Composition, Hardness
6/10
Aluminium 6060 T5, T6, T4; Aluminum Alloy 6060 Properties
8/10
Cost Efficiency
42CrMoS4 +QT (1.7227) Steel 42CrMoS4V Material Properties, Composition, Hardness
9/10
Aluminium 6060 T5, T6, T4; Aluminum Alloy 6060 Properties
7/10
Temperature Resistance
42CrMoS4 +QT (1.7227) Steel 42CrMoS4V Material Properties, Composition, Hardness
7/10
Aluminium 6060 T5, T6, T4; Aluminum Alloy 6060 Properties
4/10
Properties Comparison
| Property | 42CrMoS4 +QT (1.7227) Steel 42CrMoS4V Material Properties, Composition, Hardness | Aluminium 6060 T5, T6, T4; Aluminum Alloy 6060 Properties |
|---|---|---|
| Metal Base | Steel | Aluminum |
| Tensile Strength | 1100.0 MPa | 120.0 MPa |
| Yield Strength | 900.0 MPa | 60.0 MPa |
| Elongation | 10.0 % | 14.0 % |
| Hardness (Brinell) | — | 50.0 HB |
| Elastic Modulus | — | — |
| Density | — | — |
| Melting Point | — | — |
| Thermal Conductivity | — | — |
| Weldable | — | — |
| Heat Treatable | — | — |
| Magnetic | — | — |