6082 Aluminum Alloy 6082-T6 T651 AlMgSi1 (AlSi1MgMn – 3.2315) Properties vs T7 Tool Steel, T7A Chemical Composition, Properties & Equivalent
Ratings Comparison
Strength
6082 Aluminum Alloy 6082-T6 T651 AlMgSi1 (AlSi1MgMn – 3.2315) Properties
3/10
T7 Tool Steel, T7A Chemical Composition, Properties & Equivalent
4/10
Corrosion Resistance
6082 Aluminum Alloy 6082-T6 T651 AlMgSi1 (AlSi1MgMn – 3.2315) Properties
6/10
T7 Tool Steel, T7A Chemical Composition, Properties & Equivalent
3/10
Lightweight
6082 Aluminum Alloy 6082-T6 T651 AlMgSi1 (AlSi1MgMn – 3.2315) Properties
9/10
T7 Tool Steel, T7A Chemical Composition, Properties & Equivalent
5/10
Machinability
6082 Aluminum Alloy 6082-T6 T651 AlMgSi1 (AlSi1MgMn – 3.2315) Properties
8/10
T7 Tool Steel, T7A Chemical Composition, Properties & Equivalent
6/10
Cost Efficiency
6082 Aluminum Alloy 6082-T6 T651 AlMgSi1 (AlSi1MgMn – 3.2315) Properties
7/10
T7 Tool Steel, T7A Chemical Composition, Properties & Equivalent
9/10
Temperature Resistance
6082 Aluminum Alloy 6082-T6 T651 AlMgSi1 (AlSi1MgMn – 3.2315) Properties
4/10
T7 Tool Steel, T7A Chemical Composition, Properties & Equivalent
7/10
Properties Comparison
| Property | 6082 Aluminum Alloy 6082-T6 T651 AlMgSi1 (AlSi1MgMn – 3.2315) Properties | T7 Tool Steel, T7A Chemical Composition, Properties & Equivalent |
|---|---|---|
| Metal Base | Aluminum | Steel |
| Tensile Strength | 150.0 MPa | — |
| Yield Strength | 85.0 MPa | — |
| Elongation | 8211.0 % | — |
| Hardness (Brinell) | 40.0 HB | 187.0 HB |
| Elastic Modulus | — | — |
| Density | — | — |
| Melting Point | — | — |
| Thermal Conductivity | — | — |
| Weldable | — | — |
| Heat Treatable | — | — |
| Magnetic | — | — |