Aluminium 6060 T5, T6, T4; Aluminum Alloy 6060 Properties vs DIN EN 1.4301 Stainless Steel X5CrNi18-10 Material Equivalent, Properties, Chemical Composition
Ratings Comparison
Strength
Aluminium 6060 T5, T6, T4; Aluminum Alloy 6060 Properties
3/10
DIN EN 1.4301 Stainless Steel X5CrNi18-10 Material Equivalent, Properties, Chemical Composition
6/10
Corrosion Resistance
Aluminium 6060 T5, T6, T4; Aluminum Alloy 6060 Properties
6/10
DIN EN 1.4301 Stainless Steel X5CrNi18-10 Material Equivalent, Properties, Chemical Composition
7/10
Lightweight
Aluminium 6060 T5, T6, T4; Aluminum Alloy 6060 Properties
9/10
DIN EN 1.4301 Stainless Steel X5CrNi18-10 Material Equivalent, Properties, Chemical Composition
5/10
Machinability
Aluminium 6060 T5, T6, T4; Aluminum Alloy 6060 Properties
8/10
DIN EN 1.4301 Stainless Steel X5CrNi18-10 Material Equivalent, Properties, Chemical Composition
4/10
Cost Efficiency
Aluminium 6060 T5, T6, T4; Aluminum Alloy 6060 Properties
7/10
DIN EN 1.4301 Stainless Steel X5CrNi18-10 Material Equivalent, Properties, Chemical Composition
6/10
Temperature Resistance
Aluminium 6060 T5, T6, T4; Aluminum Alloy 6060 Properties
4/10
DIN EN 1.4301 Stainless Steel X5CrNi18-10 Material Equivalent, Properties, Chemical Composition
7/10
Properties Comparison
| Property | Aluminium 6060 T5, T6, T4; Aluminum Alloy 6060 Properties | DIN EN 1.4301 Stainless Steel X5CrNi18-10 Material Equivalent, Properties, Chemical Composition |
|---|---|---|
| Metal Base | Aluminum | Stainless Steel |
| Tensile Strength | 120.0 MPa | 540.0 MPa |
| Yield Strength | 60.0 MPa | — |
| Elongation | 14.0 % | 45.0 % |
| Hardness (Brinell) | 50.0 HB | — |
| Elastic Modulus | — | — |
| Density | — | — |
| Melting Point | — | — |
| Thermal Conductivity | — | — |
| Weldable | — | — |
| Heat Treatable | — | — |
| Magnetic | — | — |