ASTM A36 Steel Properties, Modulus of Elasticity, Yield Strength, Material Density, Hardness & Equivalent vs SAE AISI 1020 Steel Properties, C1020 Carbon Steel Yield Strength, Equivalent
Ratings Comparison
Strength
ASTM A36 Steel Properties, Modulus of Elasticity, Yield Strength, Material Density, Hardness & Equivalent
5/10
SAE AISI 1020 Steel Properties, C1020 Carbon Steel Yield Strength, Equivalent
5/10
Corrosion Resistance
ASTM A36 Steel Properties, Modulus of Elasticity, Yield Strength, Material Density, Hardness & Equivalent
3/10
SAE AISI 1020 Steel Properties, C1020 Carbon Steel Yield Strength, Equivalent
3/10
Lightweight
ASTM A36 Steel Properties, Modulus of Elasticity, Yield Strength, Material Density, Hardness & Equivalent
5/10
SAE AISI 1020 Steel Properties, C1020 Carbon Steel Yield Strength, Equivalent
5/10
Machinability
ASTM A36 Steel Properties, Modulus of Elasticity, Yield Strength, Material Density, Hardness & Equivalent
6/10
SAE AISI 1020 Steel Properties, C1020 Carbon Steel Yield Strength, Equivalent
6/10
Cost Efficiency
ASTM A36 Steel Properties, Modulus of Elasticity, Yield Strength, Material Density, Hardness & Equivalent
9/10
SAE AISI 1020 Steel Properties, C1020 Carbon Steel Yield Strength, Equivalent
9/10
Temperature Resistance
ASTM A36 Steel Properties, Modulus of Elasticity, Yield Strength, Material Density, Hardness & Equivalent
7/10
SAE AISI 1020 Steel Properties, C1020 Carbon Steel Yield Strength, Equivalent
7/10
Properties Comparison
| Property | ASTM A36 Steel Properties, Modulus of Elasticity, Yield Strength, Material Density, Hardness & Equivalent | SAE AISI 1020 Steel Properties, C1020 Carbon Steel Yield Strength, Equivalent |
|---|---|---|
| Metal Base | Steel | Steel |
| Tensile Strength | — | 380.0 MPa |
| Yield Strength | 220.0 MPa | 205.0 MPa |
| Elongation | — | 25.0 % |
| Hardness (Brinell) | — | 111.0 HB |
| Elastic Modulus | — | — |
| Density | — | — |
| Melting Point | — | — |
| Thermal Conductivity | — | — |
| Weldable | — | — |
| Heat Treatable | — | — |
| Magnetic | — | — |