DIN 1.3505 Material 100Cr6 Bearing Steel Equivalent, Composition, Properties, Hardness vs DIN EN 1.4571 Material, X6CrNiMoTi17-12-2 Stainless Steel
Ratings Comparison
Strength
DIN 1.3505 Material 100Cr6 Bearing Steel Equivalent, Composition, Properties, Hardness
8/10
DIN EN 1.4571 Material, X6CrNiMoTi17-12-2 Stainless Steel
6/10
Corrosion Resistance
DIN 1.3505 Material 100Cr6 Bearing Steel Equivalent, Composition, Properties, Hardness
3/10
DIN EN 1.4571 Material, X6CrNiMoTi17-12-2 Stainless Steel
7/10
Lightweight
DIN 1.3505 Material 100Cr6 Bearing Steel Equivalent, Composition, Properties, Hardness
5/10
DIN EN 1.4571 Material, X6CrNiMoTi17-12-2 Stainless Steel
5/10
Machinability
DIN 1.3505 Material 100Cr6 Bearing Steel Equivalent, Composition, Properties, Hardness
6/10
DIN EN 1.4571 Material, X6CrNiMoTi17-12-2 Stainless Steel
3/10
Cost Efficiency
DIN 1.3505 Material 100Cr6 Bearing Steel Equivalent, Composition, Properties, Hardness
9/10
DIN EN 1.4571 Material, X6CrNiMoTi17-12-2 Stainless Steel
6/10
Temperature Resistance
DIN 1.3505 Material 100Cr6 Bearing Steel Equivalent, Composition, Properties, Hardness
7/10
DIN EN 1.4571 Material, X6CrNiMoTi17-12-2 Stainless Steel
7/10
Properties Comparison
| Property | DIN 1.3505 Material 100Cr6 Bearing Steel Equivalent, Composition, Properties, Hardness | DIN EN 1.4571 Material, X6CrNiMoTi17-12-2 Stainless Steel |
|---|---|---|
| Metal Base | Steel | Stainless Steel |
| Tensile Strength | 1080.0 MPa | 500.0 MPa |
| Yield Strength | 835.0 MPa | 235.0 MPa |
| Elongation | 9.0 % | 40.0 % |
| Hardness (Brinell) | — | 215.0 HB |
| Elastic Modulus | — | — |
| Density | — | — |
| Melting Point | — | — |
| Thermal Conductivity | — | — |
| Weldable | — | — |
| Heat Treatable | — | — |
| Magnetic | — | — |