DIN 1.3505 Material 100Cr6 Bearing Steel Equivalent, Composition, Properties, Hardness vs SAE AISI 1020 Steel Properties, C1020 Carbon Steel Yield Strength, Equivalent
Ratings Comparison
Strength
DIN 1.3505 Material 100Cr6 Bearing Steel Equivalent, Composition, Properties, Hardness
8/10
SAE AISI 1020 Steel Properties, C1020 Carbon Steel Yield Strength, Equivalent
5/10
Corrosion Resistance
DIN 1.3505 Material 100Cr6 Bearing Steel Equivalent, Composition, Properties, Hardness
3/10
SAE AISI 1020 Steel Properties, C1020 Carbon Steel Yield Strength, Equivalent
3/10
Lightweight
DIN 1.3505 Material 100Cr6 Bearing Steel Equivalent, Composition, Properties, Hardness
5/10
SAE AISI 1020 Steel Properties, C1020 Carbon Steel Yield Strength, Equivalent
5/10
Machinability
DIN 1.3505 Material 100Cr6 Bearing Steel Equivalent, Composition, Properties, Hardness
6/10
SAE AISI 1020 Steel Properties, C1020 Carbon Steel Yield Strength, Equivalent
6/10
Cost Efficiency
DIN 1.3505 Material 100Cr6 Bearing Steel Equivalent, Composition, Properties, Hardness
9/10
SAE AISI 1020 Steel Properties, C1020 Carbon Steel Yield Strength, Equivalent
9/10
Temperature Resistance
DIN 1.3505 Material 100Cr6 Bearing Steel Equivalent, Composition, Properties, Hardness
7/10
SAE AISI 1020 Steel Properties, C1020 Carbon Steel Yield Strength, Equivalent
7/10
Properties Comparison
| Property | DIN 1.3505 Material 100Cr6 Bearing Steel Equivalent, Composition, Properties, Hardness | SAE AISI 1020 Steel Properties, C1020 Carbon Steel Yield Strength, Equivalent |
|---|---|---|
| Metal Base | Steel | Steel |
| Tensile Strength | 1080.0 MPa | 380.0 MPa |
| Yield Strength | 835.0 MPa | 205.0 MPa |
| Elongation | 9.0 % | 25.0 % |
| Hardness (Brinell) | — | 111.0 HB |
| Elastic Modulus | — | — |
| Density | — | — |
| Melting Point | — | — |
| Thermal Conductivity | — | — |
| Weldable | — | — |
| Heat Treatable | — | — |
| Magnetic | — | — |