En24 Steel Properties BS970 817M40 En24T Material Equivalent, Tempering, Strength & Hardness vs SS904L AISI 904L Stainless Steel (UNS N08904) Material Properties, Composition, Hardness
Ratings Comparison
Strength
En24 Steel Properties BS970 817M40 En24T Material Equivalent, Tempering, Strength & Hardness
2/10
SS904L AISI 904L Stainless Steel (UNS N08904) Material Properties, Composition, Hardness
5/10
Corrosion Resistance
En24 Steel Properties BS970 817M40 En24T Material Equivalent, Tempering, Strength & Hardness
3/10
SS904L AISI 904L Stainless Steel (UNS N08904) Material Properties, Composition, Hardness
7/10
Lightweight
En24 Steel Properties BS970 817M40 En24T Material Equivalent, Tempering, Strength & Hardness
5/10
SS904L AISI 904L Stainless Steel (UNS N08904) Material Properties, Composition, Hardness
5/10
Machinability
En24 Steel Properties BS970 817M40 En24T Material Equivalent, Tempering, Strength & Hardness
5/10
SS904L AISI 904L Stainless Steel (UNS N08904) Material Properties, Composition, Hardness
4/10
Cost Efficiency
En24 Steel Properties BS970 817M40 En24T Material Equivalent, Tempering, Strength & Hardness
9/10
SS904L AISI 904L Stainless Steel (UNS N08904) Material Properties, Composition, Hardness
6/10
Temperature Resistance
En24 Steel Properties BS970 817M40 En24T Material Equivalent, Tempering, Strength & Hardness
7/10
SS904L AISI 904L Stainless Steel (UNS N08904) Material Properties, Composition, Hardness
7/10
Properties Comparison
| Property | En24 Steel Properties BS970 817M40 En24T Material Equivalent, Tempering, Strength & Hardness | SS904L AISI 904L Stainless Steel (UNS N08904) Material Properties, Composition, Hardness |
|---|---|---|
| Metal Base | Steel | Stainless Steel |
| Tensile Strength | 50.0 MPa | 490.0 MPa |
| Yield Strength | — | 220.0 MPa |
| Elongation | 20.0 % | 35.0 % |
| Hardness (Brinell) | 223.0 HB | — |
| Elastic Modulus | — | — |
| Density | — | — |
| Melting Point | — | — |
| Thermal Conductivity | — | — |
| Weldable | — | — |
| Heat Treatable | — | — |
| Magnetic | — | — |