概要
AA 5182 Aluminum Alloy and AA 6016 Aluminum Alloy are both aluminum alloys commonly used in engineering applications. 5182 Aluminum offers a tensile strength of 373 MPa compared to 6016 Aluminum's 184.5 MPa.
Key Differences
- ◆ {'alloy_a': '373 MPa', 'alloy_b': '184.5 MPa', 'property': 'Tensile Strength'}
- ◆ {'alloy_a': '221.5 MPa', 'alloy_b': '161.5 MPa', 'property': 'Yield Strength'}
- ◆ {'alloy_a': 'N/A', 'alloy_b': 'N/A', 'property': 'Hardness (Brinell)'}
- ◆ {'alloy_a': 'N/A', 'alloy_b': 'N/A', 'property': 'Density'}
- ◆ {'alloy_a': 'N/A', 'alloy_b': 'N/A', 'property': 'Melting Point'}
- ◆ {'alloy_a': '5/10', 'alloy_b': '3/10', 'property': 'Strength Rating'}
- ◆ {'alloy_a': '6/10', 'alloy_b': '6/10', 'property': 'Corrosion Rating'}
- ◆ {'alloy_a': '7/10', 'alloy_b': '7/10', 'property': 'Cost Rating'}
- ◆ {'alloy_a': '8/10', 'alloy_b': '8/10', 'property': 'Machinability Rating'}
- ◆ {'alloy_a': '4/10', 'alloy_b': '4/10', 'property': 'Temperature Rating'}
- ◆ {'alloy_a': '9/10', 'alloy_b': '9/10', 'property': 'Weight Rating'}
評価比較
強度
AA 5182 Aluminum Alloy
5/10
AA 6016 Aluminum Alloy
3/10
耐食性
AA 5182 Aluminum Alloy
6/10
AA 6016 Aluminum Alloy
6/10
軽量
AA 5182 Aluminum Alloy
9/10
AA 6016 Aluminum Alloy
9/10
被削性
AA 5182 Aluminum Alloy
8/10
AA 6016 Aluminum Alloy
8/10
コスト効率
AA 5182 Aluminum Alloy
7/10
AA 6016 Aluminum Alloy
7/10
耐熱性
AA 5182 Aluminum Alloy
4/10
AA 6016 Aluminum Alloy
4/10
特性比較
| Property | AA 5182 Aluminum Alloy | AA 6016 Aluminum Alloy |
|---|---|---|
| 基本金属 | Aluminum | Aluminum |
| 引張強度 | 373.0 MPa | 184.5 MPa |
| 降伏強度 | 221.5 MPa | 161.5 MPa |
| 伸び | — | 17.5 % |
| 硬度（ブリネル） | — | — |
| 弾性率 | — | — |
| 密度 | — | — |
| 融点 | — | — |
| 熱伝導率 | — | — |
| 溶接可能 | — | — |
| 熱処理可能 | — | — |
| 磁性 | — | — |
AA 5182 Aluminum Alloy の使用場面
Choose 5182 Aluminum when you need superior strength.
AA 6016 Aluminum Alloy の使用場面
Choose 6016 Aluminum when your application specifically requires this aluminum alloy's unique combination of properties and industry certifications.
Frequently Asked Questions
Which is stronger, 5182 or 6016?
5182 has a tensile strength of 373 MPa while 6016 reaches 184.5 MPa, making 5182 the stronger alloy in ultimate tensile terms. For yield strength, 5182 is rated at 221.5 MPa versus 161.5 MPa for 6016.
Does 5182 or 6016 have better corrosion resistance?
Both alloys share the same corrosion resistance rating of 6/10.
Is 5182 or 6016 easier to weld?
Weldability data is not available for both alloys. In terms of machinability, 5182 scores 8/10 and 6016 scores 8/10.
Which is more cost-effective, 5182 or 6016?
Both alloys are similarly priced with a cost rating of 7/10.
Can I use 5182 instead of 6016 for aerospace applications?
Strength ratings: 5182 5/10 vs 6016 3/10. Always validate substitution against your specific design codes and operating conditions.