ASTM SAE AISI 1045 Carbon Steel Heat Treatment, Chemical Composition, Properties vs SAE AISI 4340 Steel Properties, Heat Treatment, Equivalent, Hardness Chart, Density, Machinability
Comparação de classificações
Resistência
ASTM SAE AISI 1045 Carbon Steel Heat Treatment, Chemical Composition, Properties
6/10
SAE AISI 4340 Steel Properties, Heat Treatment, Equivalent, Hardness Chart, Density, Machinability
5/10
Resistência à corrosão
ASTM SAE AISI 1045 Carbon Steel Heat Treatment, Chemical Composition, Properties
3/10
SAE AISI 4340 Steel Properties, Heat Treatment, Equivalent, Hardness Chart, Density, Machinability
3/10
Leve
ASTM SAE AISI 1045 Carbon Steel Heat Treatment, Chemical Composition, Properties
5/10
SAE AISI 4340 Steel Properties, Heat Treatment, Equivalent, Hardness Chart, Density, Machinability
5/10
Maquinabilidade
ASTM SAE AISI 1045 Carbon Steel Heat Treatment, Chemical Composition, Properties
6/10
SAE AISI 4340 Steel Properties, Heat Treatment, Equivalent, Hardness Chart, Density, Machinability
6/10
Eficiência de custos
ASTM SAE AISI 1045 Carbon Steel Heat Treatment, Chemical Composition, Properties
9/10
SAE AISI 4340 Steel Properties, Heat Treatment, Equivalent, Hardness Chart, Density, Machinability
9/10
Resistência à temperatura
ASTM SAE AISI 1045 Carbon Steel Heat Treatment, Chemical Composition, Properties
7/10
SAE AISI 4340 Steel Properties, Heat Treatment, Equivalent, Hardness Chart, Density, Machinability
7/10
Comparação de propriedades
| Property | ASTM SAE AISI 1045 Carbon Steel Heat Treatment, Chemical Composition, Properties | SAE AISI 4340 Steel Properties, Heat Treatment, Equivalent, Hardness Chart, Density, Machinability |
|---|---|---|
| Metal base | Steel | Steel |
| Resistência à tração | 565.0 MPa | — |
| Limite de elasticidade | 310.0 MPa | — |
| Alongamento | 16.0 % | — |
| Dureza (Brinell) | 163.0 HB | — |
| Módulo elástico | — | — |
| Densidade | — | — |
| Ponto de fusão | — | — |
| Condutividade térmica | — | — |
| Soldável | — | — |
| Tratável termicamente | — | — |
| Magnético | — | — |