MPEA Mo0.667 Nb0.667 Ti0.667 V1 Zr0.667
Embed This Widget
Add the script tag and a data attribute to embed this widget.
Embed via iframe for maximum compatibility.
<iframe src="https://alloyfyi.com/iframe/entity/mpea-mo0667-nb0667-ti0667-v1-zr0667/" width="420" height="400" frameborder="0" style="border:0;border-radius:10px;max-width:100%" loading="lazy"></iframe>Paste this URL in WordPress, Medium, or any oEmbed-compatible platform.
https://alloyfyi.com/entity/mpea-mo0667-nb0667-ti0667-v1-zr0667/Add a dynamic SVG badge to your README or docs.
[](https://alloyfyi.com/entity/mpea-mo0667-nb0667-ti0667-v1-zr0667/)Use the native HTML custom element.
Семейство: High-Entropy Alloy (MPEA)
High-entropy alloy. Phase: BCC. Processing: CAST.
Рейтинги характеристик
Performance Radar
| Свойство | Rating |
|---|---|
| Strength | 10 / 10 |
| Corrosion Res. | 5 / 10 |
| Lightweight | 6 / 10 |
| Machinability | 5 / 10 |
| Affordability | 5 / 10 |
| Heat Res. | 5 / 10 |
Состав
Механические свойства
| Предел прочности на растяжение | 3300.0 MPa |
| Предел текучести | 1735.0 MPa |
| Относительное удлинение | 20.0% |
| Твёрдость (по Роквеллу) | |
| Модуль упругости | 140.0 GPa |
Физические свойства
| Плотность | 7.100 g/cm³ |
Химический состав
| Элемент | Процентное содержание (%) |
|---|---|
| V | 1,0 |
| Mo | 0,667 |
| Nb | 0,667 |
| Ti | 0,667 |
| Zr | 0,667 |
Где купить MPEA Mo0.667 Nb0.667 Ti0.667 V1 Zr0.667
Ссылки могут приносить комиссию без дополнительных расходов для вас.
Описание
This high-entropy alloy (HEA) with nominal composition Mo0.667 Nb0.667 Ti0.667 V1 Zr0.667 is a predominantly face-centered cubic (FCC) austenitic alloy system within the multi-principal element alloy research space, incorporating Mo, Nb, Ti and 2 additional elements. Key properties include very high melting point (>1800°C), excellent high-temperature strength retention, and good oxidation resistance at elevated temperatures; molybdenum/tungsten additions provide enhanced solid-solution strengthening and creep resistance; titanium additions promote intermetallic precipitation for additional strengthening. Investigated applications include high-temperature structural applications, advanced gas turbine components, nuclear energy systems, and refractory coating materials.